Synthesis and properties of a sterically encumbered poly(thienylene vinylene): poly[E-1,2-(4,4prime-dihexyl-2,2prime-dithienyl)ethylene]

    loading  Checking for direct PDF access through Ovid

Abstract

Electrically conducting poly[E-1,2-(4,4prime-dihexyl-2,2prime-dithienyl)ethylene] was synthesized and structurally characterized by UV-visible,1H NMR, and FTIR spectroscopy. The head-to-head arrangement of the alkylthiophene dyads directly affects the UV-visible, photoluminescence, and electroluminescence maxima of the polymer. The conductivity of the doped polymer was measured to be ∼2 S cm−1 and the stability of the oxidized polymer possessing various dopants was compared. UV-visible irradiation of PDHDTE rendered the films insoluble and photolithography was used to produce micron-size images. FTIR was used to monitor the photoproducts during photolysis of PDHDTE. Mechanisms of photooxidation were proposed, based on the photoproducts observed.

On a synthétisé le poly[E-1,2-(4,4prime-dihexyl-2,2prime-dithiényl)éthylène] qui conduit l'électricité et on a caractérisé sa structure par spectroscopies UV-visible, IR à TF et RMN du1H. L'arrangement tête-à-tête des diades alkylthiophènes affecte directement les maxima du polymère dans les spectres UV-visible, la photoluminescence et l'électroluminescence. On a mesuré que la conductivité du polymère dopé est approximativement égale à 2 S cm−1 et on a comparé la stabilité du polymère oxydé comportant divers dopants. L'irradiation UV-visible du PDHDTE rend les films insolubles et on a fait appel à la photolithographie pour produire des images de la taille du micron. On a utilisé l'IR à TF pour détecter les photoproduits obtenus par photolyse de PDHDTE. On propose des mécanismes de photooxydation qui tiennent compte des photoproduits observés.

Related Topics

    loading  Loading Related Articles