Electrospun chitosan-based nanofiber mats loaded withGarcinia mangostanaextracts


    loading  Checking for direct PDF access through Ovid

Abstract

The aim of this study was to prepare electrospun chitosan-based nanofiber mats and to incorporate the fruit hull of Garcinia mangostana (GM) extracts into the mats. Chitosan-ethylenediaminetetraacetic acid/polyvinyl alcohol (CS-EDTA/PVA) was selected as the polymers. The GM extracts with 1, 2 and 3 wt% α-mangostin were incorporated into the CS-EDTA/PVA solution and electrospun to obtain nanofibers. The morphology and diameters of the mats were analyzed using scanning electron microscopy (SEM). The mechanical and swelling properties were investigated. The amount of GM extracts was determined using high-performance liquid chromatography (HPLC). The antioxidative activity, antibacterial activity, extract release and stability of the mats were evaluated. In vivo wound healing tests were also performed in Wistar rats. The results indicated that the diameters of the fibers were on the nanoscale and that no crystals of the extract were observed in the mats at any concentration. The mats provided suitable tensile strength and swelling properties. All of the mats exhibited antioxidant and antibacterial activity. During the wound healing test, the mats accelerated the rate of healing when compared to the control (gauze-covered). The mats maintained 90% of their content of α-mangostin for 3 months. In conclusion, the chitosan-based nanofiber mats loaded with GM extracts were successfully prepared using the electrospinning method. These nanofiber mats loaded with GM extracts may provide a good alternative for accelerating wound healing.

    loading  Loading Related Articles