The Effect of Temporary Cement Cleaning Methods on the Retention of Crowns.
To evaluate the effect of temporary cement cleaning methods on the retention of cemented crowns using zinc phosphate cement and resin-modified glass ionomer cement.MATERIALS AND METHODS
Forty titanium specimens were fabricated to simulate prepared molars with minimally retentive taper. The Ni-Cr cast crowns were fabricated, temporarily cemented, and separated. The specimens were divided into four groups according to the temporary cement cleaning method (n = 10) as follows: control group (no temporary cementation), orange solvent group, ultrasonic cleaning group, and air-abrasion group. After the cleaning procedures, the specimens were cemented with definitive cements (zinc phosphate cement and resin-modified glass ionomer, RMGI, cement) and subjected to thermocycling (5000 cycles, 5-55°C, dwell time, 10 seconds). The tensile bond strength of each specimen was measured using a universal testing machine, and the results were analyzed using the Kruskal-Wallis and Mann-Whitney U test (α = 0.05).RESULTS
When cemented with zinc phosphate cement, the statistical analysis showed that the value of the air-abrasion group was significantly higher than those of the other groups (p < 0.01). There was no statistically significant difference among the other groups. When cemented with RMGI cement, the air-abrasion group showed the lowest value, and the control group showed the highest value (p < 0.01). The difference between the ultrasonic cleaning group and the orange solvent group was not statistically significant.CONCLUSION
The use of temporary cement did not have a significant influence on retention of permanently cemented crowns when zinc phosphate cement was used for permanent cementation. Airborne-particle abrasion after provisional cementation improved retention of crowns cemented with zinc phosphate cement; however, the use of temporary cement significantly decreased retention of permanently cemented crowns when RMGI cement was used regardless of the temporary cement cleaning method.